Use of waste gypsum to replace natural gypsum as set retarders in portland cement

Chandara, Chea ; Azizli, Khairun Azizi Mohd ; Ahmad, Zainal Arifin ; Sakai, Etsuo

Waste Management, 15 May 2009, Vol.29(5) [Tạp chí có phản biện]

ISSN: 0956-053X ; E-ISSN: 1879-2456 ; DOI: 10.1016/j.wasman.2008.11.014

Toàn văn sẵn có

Trích dẫn Trích dẫn bởi
  • Nhan đề:
    Use of waste gypsum to replace natural gypsum as set retarders in portland cement
  • Tác giả: Chandara, Chea ; Azizli, Khairun Azizi Mohd ; Ahmad, Zainal Arifin ; Sakai, Etsuo
  • Chủ đề: Materials Science ; Calorimetry ; Ceramics ; Compression Strength ; Fluorescence ; Gypsum ; Gypsum Cements ; Hydrates ; Hydration ; Portland Cement ; Thermal Gravimetric Analysis ; Wastes ; X-Ray Diffraction ; X-Ray Fluorescence Analysis ; Engineering ; Chemistry
  • Là 1 phần của: Waste Management, 15 May 2009, Vol.29(5)
  • Mô tả: The present study is focused on clarifying the influence of waste gypsum (WG) in replacing natural gypsum (NG) in the production of ordinary Portland cement (OPC). WG taken from slip casting moulds in a ceramic factory was formed from the hydration of plaster of paris. Clinker and 3-5 wt% of WG was ground in a laboratory ball mill to produce cement waste gypsum (CMWG). The same procedure was repeated with NG to substitute WG to prepare cement natural gypsum (CMNG). The properties of NG and WG were investigated via X-ray Diffraction (XRD), X-ray fluorescence (XRF) and differential scanning calorimetry (DSC)/thermogravimetric (TG) to evaluate the properties of CMNG and CMWG. The mechanical properties of cement were tested in terms of setting time, flexural and compressive strength. The XRD result of NG revealed the presence of dihydrate while WG contained dihydrate and hemihydrate. The content of dihydrate and hemihydrates were obtained via DSC/TG, and the results showed that WG and NG contained 12.45% and 1.61% of hemihydrate, respectively. Furthermore, CMWG was found to set faster than CMNG, an average of 15.29% and 13.67% faster for the initial and final setting times, respectively. This was due to the presence of hemihydrate in WG. However, the values obtained for flexural and compressive strength were relatively the same for CMNG and CMWG. Therefore, this result provides evidence that WG can be used as an alternative material to NG in the production of OPC.